PA 6C Moly Filled
Improved crystallisation and a degree of self-lubrication occur by the addition of molybdenum disulphide. Hardness increases and simultaneously the general mechanical and anti-friction properties are improved.
Key features
- Increased superficial hardness provides excellent machineability
- Improvement in wear properties as a result of dry lubricant
- Improved anti-friction properties
- Improved mechanical properties
- Elevated operating temperatures
- Improved dimensional stability
- Excellent chemical resistance properties
- Good PV and load bearing capabilities
- Extended range of applications
Properties
| Property |
Unit of measure |
Value |
| Tensile Strength | Mpa | 85 |
| Elongation at Break | % | >20 |
| Modulus of Elasticity | MPa | 4100 |
| Impact Strength | kj/m² | 4.50 |
| Compressive Strength | MPa | 105 |
| Shear Strength | MPa | |
| Shore Hardness | D Scale | 85 |
| Co-efficient of Friction | μ | 0.25 |
| Water Absorption @ 23 Deg C | % | 7.00 |
| Service Temperature Intermittent | ᵒC | 170 |
| Service Temperature Continuous | ᵒC | 105 |
| Melting point | ᵒC | 220 - 225ºC |
| Thermal Conductivity | W/m.ᵒC | 0.26 |
| Dielectric Strength | kV/mm | 25 |
| Volume Resistivity | Ω.cm | 10¹³ |
| Surface Resistivity | Ω | 10¹² |
| Arc Resistance | Sec | |